(110) [001] Grain Growth in Silicon Steel Sheets of 30 µm Thickness

M. Nakano, S. Agatsuma, K. Ishiyama, K. I. Arai

Research output: Contribution to journalArticlepeer-review

1 Citation (Scopus)


Thin grain-oriented silicon steel sheets have the lowest iron loss at a thickness of 30 µm. We observed the recrystallization behavior and magnetic properties of 30 µm thick silicon steel sheets, and compared the results with those of 60 µm thick silicon steel sheets. The recrystallization processes in the two types of sheet were found to be different. The primary recrystallized 30 µm thick silicon steel sheets did not have a strong (110) [001] texture or other orientation; consequently secondary recrystallization did not occur. However, at annealing temperatures above 1050°C, (110) [001] grains grew selectively. Thus we were able to obtain very thin grain-oriented silicon steel sheets with a thickness of 30 µm.

Original languageEnglish
Pages (from-to)67-72
Number of pages6
JournalIEEE Translation Journal on Magnetics in Japan
Issue number1
Publication statusPublished - 1994


Dive into the research topics of '(110) [001] Grain Growth in Silicon Steel Sheets of 30 µm Thickness'. Together they form a unique fingerprint.

Cite this