Al insertion and additive effects on the thermoelectric properties of yttrium boride

Satofumi Maruyama, Anastasiia Prytuliak, Yuzuru Miyazaki, Kei Hayashi, Tsuyoshi Kajitani, Takao Mori

Research output: Contribution to journalArticlepeer-review

22 Citations (Scopus)


The aluminoboride YxAlyB14 (x∼0.57, 0.41 ≤ y ≤ 0.63) has been found to show striking p-n control of the thermoelectric properties through variations of the y occupancy of the Al site. The effect of Al was investigated in further extremes. Polycrystalline samples of Al-free YxB14(x∼0.55; "YB25") were successfully synthesized in sufficient amounts for bulk spark plasma sintering (SPS) samples and their thermoelectric properties were investigated. Y0.56Al0.57B14 was also prepared in comparison, and further Al was added to the samples through SPS treatment. We observed that Y0.55B14 exhibits large positive Seebeck coefficients, ∼1000μV K-1, around room temperature and the absolute value of the Seebeck coefficient largely decreases with increase of temperature while that of Y0.56Al0.57B14 is proportional to T-1/2, indicating a strong effect of Al on the electronic structure around the Fermi level. Y0.55B14 was found to be strongly disordered with a relatively low thermal conductivity and short localization length of 0.65Å which is close to that previously determined for the disordered and thermally glass-like compound YB66. Occupancy of Al could not be increased further for the Al-rich sample, although Al was discovered to act as a sintering aid to enhance density and ZT could be significantly improved by 50%.

Original languageEnglish
Article number123702
JournalJournal of Applied Physics
Issue number12
Publication statusPublished - 2014 Mar 28


Dive into the research topics of 'Al insertion and additive effects on the thermoelectric properties of yttrium boride'. Together they form a unique fingerprint.

Cite this