Carrier dependent cell differentiation of bone morphogenetic protein-2 induced osteogenesis and chondrogenesis during the early implantation stage in rats

To evaluate the osteoinductive effects of recombinant human bone morphogenetic protein (rhBMP)-2 during the early stages of rat ectopic bone formation, we prepared two distinct carriers. Two carriers, insoluble bone matrix (IBM) and fibrous glass membrane (FGM) were combined with rhBMP-2 and implanted into the backs of rats to evaluate the osteoinductive effects of the two rhBMP-2 carrier systems. Insoluble bone matrix particle size was 320 to 620 μm. Fibrous glass membrane was constructed from unwoven glass fibers 1 μm in diameter. Alkaline phosphatase (ALP) activity and type II collagen were detected in IBM/rhBMP-2 at 5 days postimplantation. Calcium (Ca) was also detected in IBM/rhBMP-2 at 7 and 9 days postimplantation. In contrast, ALP and type II collagen were detected in FGM/rhBMP-2 at 7 days. Calcium was undetected, indicating that the bone formation in IBM/rhBMP-2 proceeded faster than in FGM/rhBMP-2 during the early stage of BMP-induced osteogenesis. In addition, mRNA expression level of KDR, a receptor for vascular endothelial growth factor, was also increased in IBM/rhBMP-2. To investigate the in vivo release profile of rhBMP-2, iodine 125 (¹²⁵I)-labeled BMP-2-incorporating IBM and FGM implants were inserted into the back subcutis of mice. More than 60% of the rhBMP-2 was released from the IBM/rhBMP-2 carrier within 1 day after implantation, whereas 50% of the rhBMP-2 was released from the FGM/rhBMP-2 10 days postimplantation. These results indicated that osteo- and chondrogenesis depends highly upon the geometry of the carrier and the in situ retention of rhBMP-2 during the early stage of rhBMP-2 induced bone formation.