Crystal structure and compositional analysis of epitaxial (K0.56Na0.44)NbO3 films prepared by hydrothermal method

Takahisa Shiraishi, Hiro Einishi, Takao Shimizu, Hiroshi Funakubo, Minoru Kurosawa, Hiroshi Uchida, Nobuhiro Kumada, Takanori Kiguchi, Toyohiko J. Konno

Research output: Contribution to journalArticlepeer-review

6 Citations (Scopus)


(KxNa1-x)NbO3 films were deposited on Nb-doped (100)SrTiO3 substrates at 240 °C for times between 1 and 6 h by a hydrothermal method. Over this time series, the measured (K + Na)/Nb ratio of the films was found to remain constant, but the bulk K/(K + Na) ratio, x, decreased from an initial value of 0.75-0.56. It was determined that film growth initially proceeded through crystallization of the K-rich phase (K0.75Na0.25)NbO3. For film growth times greater than 3 h, a second perovskite phase with a smaller unit cell volume was detected, with an estimated composition of (K0.36Na0.64)NbO3. As such, the measured bulk composition value x = 0.56 was determined to be the result of a combination of these two phases, as opposed to originating from a single phase. Cross-sectional transmission electron microscopy analyses of films prepared for 6 h revealed that they consist of two layers in the direction normal to the substrate; this bilayer-type structure, only observed for hydrothermal growth of this material, is considered to arise from the large solubility mismatch between the Nb precursor and KOH and NaOH in the growth solution.

Original languageEnglish
Pages (from-to)693-701
Number of pages9
JournalJournal of Materials Research
Issue number6
Publication statusPublished - 2016 Mar 28


  • crystallographic structure
  • film
  • hydrothermal


Dive into the research topics of 'Crystal structure and compositional analysis of epitaxial (K0.56Na0.44)NbO3 films prepared by hydrothermal method'. Together they form a unique fingerprint.

Cite this