TY - JOUR
T1 - Development of high field heat-treatment equipment and relevant applications
AU - Watanabe, Kazuo
AU - Awaji, Satoshi
AU - Kimura, Keiichi
PY - 1997
Y1 - 1997
N2 - High field and high temperature heat-treatment equipment was developed, using an 11 T liquid helium-free superconducting magnet with a 52 mm diameter room temperature bore. The newly developed heat-treatment system enables us to carry out an experiment, continuously, at 10 T and at temperatures up to 1200 °C for a few weeks or months. As a performance test, a high field seeding process for YBa2Cu3O7 bulk at 10 T and about 1000 °C for 3 days is developed, to improve the crystallinity of the YBa2Cu3O7 bulk.
AB - High field and high temperature heat-treatment equipment was developed, using an 11 T liquid helium-free superconducting magnet with a 52 mm diameter room temperature bore. The newly developed heat-treatment system enables us to carry out an experiment, continuously, at 10 T and at temperatures up to 1200 °C for a few weeks or months. As a performance test, a high field seeding process for YBa2Cu3O7 bulk at 10 T and about 1000 °C for 3 days is developed, to improve the crystallinity of the YBa2Cu3O7 bulk.
UR - http://www.scopus.com/inward/record.url?scp=0031167513&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=0031167513&partnerID=8YFLogxK
U2 - 10.1143/jjap.36.l673
DO - 10.1143/jjap.36.l673
M3 - Article
AN - SCOPUS:0031167513
SN - 0021-4922
VL - 36
SP - L673-L675
JO - Japanese Journal of Applied Physics
JF - Japanese Journal of Applied Physics
IS - 6 A
ER -