Effects of carbon addition on mechanical properties and microstructures of Ni-Free Co-Cr-W-based dental alloys

Research output: Chapter in Book/Report/Conference proceedingChapterpeer-review

1 Citation (Scopus)


We investigated the effects of carbon concentration on the microstructures and tensile properties of Ni-free Co-29Cr-9W-1Si-C (mass%) alloys used as disk materials in dental technology based on computer-aided design and computer-aided manufacturing (CAD/CAM). The alloy specimens, which contained carbon in different concentrations, were prepared by conventional casting. The precipitates changed from intermetallic compounds in the low-carbon alloys, e.g., the s and Laves phases, to M23C6-type carbide (M: metal) with increasing bulk carbon concentration. M23C6 dramatically enhanced the 0.2% proof stress, which then gradually increased with increasing carbon content in the alloys. The elongation-to-failure also increased with increasing carbon content. The coarse M23C6 particles formed by higher concentrations of carbon were detrimental to ductility, however, and a maximum elongation-to-failure was obtained at a carbon concentration of ~0.1 mass%. In addition, we applied hot-deformation processing to the cast-alloy specimens and revealed that compared to as-cast alloys, the hot-rolled alloys with added carbon showed an excellent combination of high strength and high ductility. The current study can thus aid in the design of biomedical, carbon-containing, Co-28Cr-9W-1Si-based alloys.

Original languageEnglish
Title of host publicationInterface Oral Health Science 2014
Subtitle of host publicationInnovative Research on Biosis-Abiosis Intelligent Interface
PublisherSpringer Japan
Number of pages12
ISBN (Electronic)9784431551928
ISBN (Print)9784431551256
Publication statusPublished - 2015 Jan 1


  • Biomedical co-cr-w alloy
  • Carbon addition
  • Mechanical properties
  • Microstructures
  • Precipitation


Dive into the research topics of 'Effects of carbon addition on mechanical properties and microstructures of Ni-Free Co-Cr-W-based dental alloys'. Together they form a unique fingerprint.

Cite this