Electrical and magnetic properties of chemically derived nanocrystalline cobalt ferrite

N. Sivakumar, A. Narayanasamy, K. Shinoda, C. N. Chinnasamy, B. Jeyadevan, J. M. Greneche

Research output: Contribution to journalArticlepeer-review

87 Citations (Scopus)


Nanocrystalline cobalt ferrite particles of 8 nm grain size were synthesized by coprecipitation technique and subsequently suitably heat treated to obtain higher grain sizes. The experimentally observed changes in the dc electrical conductivity and Curie temperature with heat treatment have been attributed to the changes in the cation distributions as obtained from the Mössbauer and extended x-ray absorption fine structure (EXAFS) measurements and to the grain size. The activation energies for conduction as determined from the Arrhenius plots suggest that the conductivity is due to hopping of both electrons and holes. The observed decrease in conductivity when the grain size is increased from 8 to 92 nm is clearly due to the predominant effect of migration of some of the Fe3+ ions from octahedral to tetrahedral sites, as is evident from in-field Mössbauer and EXAFS measurements. But the higher conductivity of the 102 and 123 nm particles compared to that of the 92 nm particles is attributed to the higher grain size, since the cation distribution is found to be the same for all these three samples. The Ńel temperature increases from 709 K for the as-prepared particles (8 nm) to 809 K for the 92 nm particles because of the change in the cation distribution and it remains almost the same for the higher grain sizes as there is no further change in the cation distribution.

Original languageEnglish
Article number013916
JournalJournal of Applied Physics
Issue number1
Publication statusPublished - 2007


Dive into the research topics of 'Electrical and magnetic properties of chemically derived nanocrystalline cobalt ferrite'. Together they form a unique fingerprint.

Cite this