Electron beam irradiation-induced reduction of SnO2 deposited on TiO2(110) surfaces

Yutaro Komuro, Yuji Matsumoto

Research output: Contribution to journalArticlepeer-review

8 Citations (Scopus)


SnO2 was deposited by pulsed laser deposition at room temperature in ultrahigh vacuum on TiO2(110) surfaces having different chemical states, either fully oxidized TiO2(110)-(1 × 1) or partially reduced TiO2(110)-(1 × 2). For both cases, just after deposition, Sn was found to be in an oxidized state. When the SnO2 on TiO2 surfaces was irradiated with an electron beam, SnO2 was completely reduced into a metallic state, with the reduction rate of SnO2 on the TiO2(110)-(1 × 2) surface being at least 3 times higher than that on TiO2(110)-(1 × 1). Scanning tunneling microscopy images of SnO2 on a TiO2(110)-(1 × 2) surface, measured before and after electron beam irradiation, suggest that, while SnO2 is reduced into a metal, the reduced TiO2(110)-(1 × 2) surface is simultaneously reoxidized, consequently decomposing the (1 × 2) reconstruction.

Original languageEnglish
Pages (from-to)6618-6621
Number of pages4
JournalJournal of Physical Chemistry C
Issue number14
Publication statusPublished - 2011 Apr 14


Dive into the research topics of 'Electron beam irradiation-induced reduction of SnO2 deposited on TiO2(110) surfaces'. Together they form a unique fingerprint.

Cite this