N2 - In this study, we investigated the hydrogen absorption behavior of pre-rusted steel in an NaCl droplet by measuring the hydrogen permeation current and corrosion potential. To prepare the pre-rusted steel, a 30-μL droplet of a 0.1-mol/dm3 NaCl solution was placed on the surface of steel and exposed to wet-dry cyclic conditions by changing the relative humidity (RH) repeatedly from 40% to 95% at a constant rate of 27.5%/h and 298 K. The hydrogen permeation current and corrosion potential of the pre-rusted steel were measured during the drying of an electrolyte droplet using an electrochemical hydrogen permeation test and the Kelvin probe (KP) technique, respectively. The corrosion potential of the pre-rusted steel shifted in the negative direction simultaneous with the evolution of the hydrogen permeation current during the drying of the droplet. The hydrogen permeation current increased with the number of wet-dry cycles in the early stages of the rusting process, which related to the negative shift in corrosion potential. As the whole surface of the steel was covered with iron rust in the later stages of the rusting process, the corrosion potential shifted in the positive direction and the hydrogen absorption current decreased gradually.
AB - In this study, we investigated the hydrogen absorption behavior of pre-rusted steel in an NaCl droplet by measuring the hydrogen permeation current and corrosion potential. To prepare the pre-rusted steel, a 30-μL droplet of a 0.1-mol/dm3 NaCl solution was placed on the surface of steel and exposed to wet-dry cyclic conditions by changing the relative humidity (RH) repeatedly from 40% to 95% at a constant rate of 27.5%/h and 298 K. The hydrogen permeation current and corrosion potential of the pre-rusted steel were measured during the drying of an electrolyte droplet using an electrochemical hydrogen permeation test and the Kelvin probe (KP) technique, respectively. The corrosion potential of the pre-rusted steel shifted in the negative direction simultaneous with the evolution of the hydrogen permeation current during the drying of the droplet. The hydrogen permeation current increased with the number of wet-dry cycles in the early stages of the rusting process, which related to the negative shift in corrosion potential. As the whole surface of the steel was covered with iron rust in the later stages of the rusting process, the corrosion potential shifted in the positive direction and the hydrogen absorption current decreased gradually.
UR - http://www.scopus.com/inward/record.url?scp=85073205554&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=85073205554&partnerID=8YFLogxK
U2 - 10.1149/2.0591910jes
DO - 10.1149/2.0591910jes
M3 - Article
AN - SCOPUS:85073205554
SN - 0013-4651
VL - 166
SP - C243-C249
JO - Journal of the Electrochemical Society
JF - Journal of the Electrochemical Society
IS - 10
ER -