Abstract
This study investigated the effect of aging and thermomechanical treatments on the mechanical properties of a nanocluster-strengthened ferritic steel, Fe-1.5Mn-2.5Cu-4.0Ni-1.0Al (wt pct). The effect of thermomechanical treatments on the microhardness and tensile properties were measured at room temperature and correlated with microstructural features. Cu-rich precipitates were characterized by transmission electron microscopy and were found to coarsen slowly during long-time aging. The microhardness measurements indicate a typical precipitation hardening behavior during aging at 773 K (500 °C). Tensile tests showed that thermomechanical treatments can improve the mechanical strength and ductility of the nanocluster-strengthened ferritic steel significantly compared with those without the treatments. Fractography results indicated that the high yield strength resulted from precipitation hardening makes the steel more susceptible to grain-boundary decohesion, which can be suppressed by grain refinement. Atmosphere adsorption and diffusion along grain boundaries were found to intensify brittle intergranular fracture, and this embrittlement can be avoided by vacuum heat treatment.
| Original language | English |
|---|---|
| Pages (from-to) | 351-359 |
| Number of pages | 9 |
| Journal | Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science |
| Volume | 43 |
| Issue number | 1 |
| DOIs | |
| Publication status | Published - 2012 Jan |
ASJC Scopus subject areas
- Condensed Matter Physics
- Mechanics of Materials
- Metals and Alloys