T1 - Mechanical Properdes of TiC0.5N0.5-Mo2C-Ni Alloy in Reladon to Mo2C Content
AU - Suzuki, Hisashi
AU - Matsubara, Hideaki
AU - Asano, Masaya
PY - 1985
Y1 - 1985
N2 - TiC0.5N0.5-(2∼18)vol%Mo2C-16.4 vol%Ni alloys were sintered and HIP-treated at 1723 K, and then resintered at 1823 K. The microstructure, transverse-rupture strength at room temperature and 1273 K, etc. of the alloys were studied in relation to Mo2C content. The TRS at room temperature of the resintered alloy increased with increasing Mo2C content and attained a maximum with the Mo2C content of about 10%. The TRS and resistance to deformation at 1273 K became higher with increasing Mo2C content. The discussions on these results were given.
AB - TiC0.5N0.5-(2∼18)vol%Mo2C-16.4 vol%Ni alloys were sintered and HIP-treated at 1723 K, and then resintered at 1823 K. The microstructure, transverse-rupture strength at room temperature and 1273 K, etc. of the alloys were studied in relation to Mo2C content. The TRS at room temperature of the resintered alloy increased with increasing Mo2C content and attained a maximum with the Mo2C content of about 10%. The TRS and resistance to deformation at 1273 K became higher with increasing Mo2C content. The discussions on these results were given.
UR - http://www.scopus.com/inward/record.url?scp=0022151863&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=0022151863&partnerID=8YFLogxK
U2 - 10.2497/jjspm.32.301
DO - 10.2497/jjspm.32.301
M3 - Article
AN - SCOPUS:0022151863
SN - 0532-8799
VL - 32
SP - 301
EP - 304
JO - Funtai Oyobi Fummatsu Yakin/Journal of the Japan Society of Powder and Powder Metallurgy
JF - Funtai Oyobi Fummatsu Yakin/Journal of the Japan Society of Powder and Powder Metallurgy
IS - 8
ER -