Various types of coating films were obtained from hydrothermally synthesized Nb-doped TiO2 (NTO) and CsxWO3 (CWO) nanoparticles. The coating films possessed multifunctionality including near infrared (NIR) absorption and photocatalysis abilities. The NTO and CWO nanoparticles were synthesized by a unique solvothermal reaction in which water induced by an esterification reaction between alcohol and carboxylic acid can act as a hydrolyzing agent for metal precursors. NTO was synthesized by the unique solvothermal reaction for the first time. The reaction accompanied by the reduction of Ti4+ to Ti3+ led to the formation of nanoparticles with both NIR absorption and photocatalytic properties. The effect of the ethanol-acetic acid ratio on the morphology of the obtained NTO was investigated, and the larger amount of acetic acid led to a larger nanoparticle size, indicating the size controllability. The two types of coating film, including CWO and NTO nanoparticles, were obtained for comparison: (1) coexistent coating film: one side of the quartz glass was coated with a dispersion, including both CWO and NTO nanoparticles, and (2) double-sided coating film: a quartz glass coated with a CWO dispersion on one side and an NTO dispersion on the other side. The double-sided coating led to higher multifunctionality. Furthermore, the optimized condition for the double-sided coating was investigated by using various NTO particles obtained using different ethanol-acetic acid ratios.
- multifunctional coating
- Nb-doped TiO
- near infrared shielding
- photocatalytic NOx decomposition