Self-ordering behavior of anodic porous alumina via selenic acid anodizing

Tatsuya Kikuchi, Osamu Nishinaga, Shungo Natsui, Ryosuke O. Suzuki

Research output: Contribution to journalArticlepeer-review

75 Citations (Scopus)


The self-ordering behavior of anodic porous alumina that was formed by anodizing in selenic acid electrolyte (H2SeO4) at various concentrations and voltages was investigated with SEM and AFM imaging. A high purity aluminum foil was anodized in 0.1-3.0 M selenic acid solutions at 273 K and at constant cell voltages in the range of 37 to 51 V. The regularity of the cell arrangement increased with increasing anodizing voltage and selenic acid concentration under conditions of steady oxide growth without burning. Anodizing at 42-46 V in 3.0 M selenic acid produced highly ordered porous alumina. By selective dissolution of the anodic porous alumina, highly ordered convex nanostructures of aluminum with diameters of 20 nm and heights of 40 nm were exposed at the apexes of each hexagonal dimple array. Highly ordered anodic porous alumina with a cell size of 102 nm from top to bottom can be fabricated by a two-step selenic acid anodizing process, that includes the first anodizing step, the selective oxide dissolution, and the second anodizing step.

Original languageEnglish
Pages (from-to)728-735
Number of pages8
JournalElectrochimica Acta
Publication statusPublished - 2014 Aug 10


  • Aluminum
  • Anodic Porous Alumina
  • Anodizing
  • Selenic Acid


Dive into the research topics of 'Self-ordering behavior of anodic porous alumina via selenic acid anodizing'. Together they form a unique fingerprint.

Cite this