Synthesis and magnetic properties of Zn2+ stabilized La M-type ferrite

Hirofumi Kakuta, Ryo Murakami, Hitoshi Takamura, Terumi Tanaka, Motofumi Homma, Masuo Okada

Research output: Contribution to journalArticlepeer-review

6 Citations (Scopus)


The crystal structure and magnetic properties of Zn-stabilized La M-type ferrite with magnetoplumbite structure were studied. The single phase of M-type ferrite was obtained by using conventional ceramic techniques with nominal composition of LaZn0.5Fe11.3O19. It was confirmed that the Zn-stabilized La M-type ferrite had a hexagonal symmetry (P63/mmc) with lattice constants of a=0.5890, c=2.2926nm. The c-axis length was smaller than that of Sr or Ba M-type ferrite. The magnetization of this ferrite is 81.4μWb·m·kg-1 at room temperature at the applied field of 1200kA·m-1, and the Curie temperature is 649K.

Original languageEnglish
Pages (from-to)22-26
Number of pages5
JournalFuntai Oyobi Fummatsu Yakin/Journal of the Japan Society of Powder and Powder Metallurgy
Issue number1
Publication statusPublished - 1997 Jan


  • Lanthanum-zinc ferrite
  • M-type ferrite
  • Rietveld analysis


Dive into the research topics of 'Synthesis and magnetic properties of Zn2+ stabilized La M-type ferrite'. Together they form a unique fingerprint.

Cite this