部分還元処理による鉄鉱石中りんのダイカルシウムシリケート相への濃化

Nobuhiro Maruoka; Hironari Kubo

doi:10.2355/tetsutohagane.TETSU-2020-082

部分還元処理による鉄鉱石中りんのダイカルシウムシリケート相への濃化

Nobuhiro Maruoka, Hironari Kubo

多元物質科学研究所・プロセスシステム工学研究部門

研究成果: Article › 査読

抄録

It is necessary to develop an innovative iron-making technology for low-grade iron ore containing a high concentration of P. In this study, we propose a new process for enriching phosphorus in the C₂S phase by mixing high-P iron ore, CaO, and graphite in appropriate proportions and partially reducing it. In this study, high-P iron ore adjusted to various basicities and reducing agent ratios was heated at 1573 K in Ar atmosphere, and the obtained sample was analyzed by EPMA. The results showed that in the reduced sample obtained under the conditions of C/S = 2.0 and Target Fe_tO = 60%, more than 95% of P was distributed to the C₂S phase, and the P content in metallic iron was sufficiently low.

寄稿の翻訳タイトル	Enrichment of Phosphorus from Iron Ore to Dicalcium-silicate Phase by Partial Reduction
本文言語	Japanese
ページ（範囲）	527-533
ページ数	7
ジャーナル	Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan
巻	107
号	6
DOI	https://doi.org/10.2355/tetsutohagane.TETSU-2020-082
出版ステータス	Published - 2021 6月 1

Keywords

Dicalcium silicate
Ironmaking
Low grade ore
Phosphorous
Separation

ASJC Scopus subject areas

凝縮系物理学
物理化学および理論化学
金属および合金
材料化学

文献へのアクセス

10.2355/tetsutohagane.TETSU-2020-082

他のファイルとリンク

引用スタイル

@article{b5ed2d3ecb2043c6a131d4090069e50b,

title = "部分還元処理による鉄鉱石中りんのダイカルシウムシリケート相への濃化",

abstract = "It is necessary to develop an innovative iron-making technology for low-grade iron ore containing a high concentration of P. In this study, we propose a new process for enriching phosphorus in the C2S phase by mixing high-P iron ore, CaO, and graphite in appropriate proportions and partially reducing it. In this study, high-P iron ore adjusted to various basicities and reducing agent ratios was heated at 1573 K in Ar atmosphere, and the obtained sample was analyzed by EPMA. The results showed that in the reduced sample obtained under the conditions of C/S = 2.0 and Target FetO = 60%, more than 95% of P was distributed to the C2S phase, and the P content in metallic iron was sufficiently low.",

keywords = "Dicalcium silicate, Ironmaking, Low grade ore, Phosphorous, Separation",

author = "Nobuhiro Maruoka and Hironari Kubo",

note = "Publisher Copyright: {\textcopyright} 2021 The Iron and Steel Institute of Japan",

year = "2021",

month = jun,

day = "1",

doi = "10.2355/tetsutohagane.TETSU-2020-082",

language = "Japanese",

volume = "107",

pages = "527--533",

journal = "Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan",

issn = "0021-1575",

publisher = "Iron and Steel Institute of Japan",

number = "6",

}

TY - JOUR

T1 - 部分還元処理による鉄鉱石中りんのダイカルシウムシリケート相への濃化

AU - Maruoka, Nobuhiro

AU - Kubo, Hironari

PY - 2021/6/1

Y1 - 2021/6/1

N2 - It is necessary to develop an innovative iron-making technology for low-grade iron ore containing a high concentration of P. In this study, we propose a new process for enriching phosphorus in the C2S phase by mixing high-P iron ore, CaO, and graphite in appropriate proportions and partially reducing it. In this study, high-P iron ore adjusted to various basicities and reducing agent ratios was heated at 1573 K in Ar atmosphere, and the obtained sample was analyzed by EPMA. The results showed that in the reduced sample obtained under the conditions of C/S = 2.0 and Target FetO = 60%, more than 95% of P was distributed to the C2S phase, and the P content in metallic iron was sufficiently low.

AB - It is necessary to develop an innovative iron-making technology for low-grade iron ore containing a high concentration of P. In this study, we propose a new process for enriching phosphorus in the C2S phase by mixing high-P iron ore, CaO, and graphite in appropriate proportions and partially reducing it. In this study, high-P iron ore adjusted to various basicities and reducing agent ratios was heated at 1573 K in Ar atmosphere, and the obtained sample was analyzed by EPMA. The results showed that in the reduced sample obtained under the conditions of C/S = 2.0 and Target FetO = 60%, more than 95% of P was distributed to the C2S phase, and the P content in metallic iron was sufficiently low.

KW - Dicalcium silicate

KW - Ironmaking

KW - Low grade ore

KW - Phosphorous

KW - Separation

UR - http://www.scopus.com/inward/record.url?scp=85107384328&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=85107384328&partnerID=8YFLogxK

U2 - 10.2355/tetsutohagane.TETSU-2020-082

DO - 10.2355/tetsutohagane.TETSU-2020-082

M3 - Article

AN - SCOPUS:85107384328

SN - 0021-1575

VL - 107

SP - 527

EP - 533

JO - Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan

JF - Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan

IS - 6

ER -

部分還元処理による鉄鉱石中りんのダイカルシウムシリケート相への濃化

抄録

Keywords

ASJC Scopus subject areas

文献へのアクセス

他のファイルとリンク

フィンガープリント

引用スタイル