Comparison of corrosion resistances between Fe2O3-TiO2 artificial passivation film and passivation film on Fe-Ti alloy

Hyunsoo Kim, Noboru Akao, Nobuyoshi Hara, Katsuhisa Sugimoto

研究成果: ジャーナルへの寄稿総説査読

15 被引用数 (Scopus)

抄録

Fe2O3-TiO2 double-oxide films were formed on Pt substrates by low-pressure metallorganic chemical vapor deposition using iron acetylacetonate and tetraisopropoxytitanium as precursors and O2 as a reaction gas. Fe-Ti alloys were fabricated by an ion-beam sputter and an arc-melting process. The corrosion resistances of the Fe2O3-TiO2 films and the Fe-Ti alloys were examined in acid solutions. The thinning rate of the Fe2O3-TiO2 films in 5 M HCl decreased with an increase in the formation temperature. Likewise, the dissolution rate decreased with increasing titanium cationic fraction in the films. The films hardly dissolved at anodic potentials, while significant dissolution occurred at cathodic potentials in 1 M H2SO4 owing to the selective reduction of iron oxide components in the films. Sputter-deposited Fe-Ti alloy films containing more than 39 atom % Ti and arc-melted Fe-Ti alloys containing more than 57 atom % Ti showed high corrosion resistance when passivated anodically in 5 M HCl. The dissolution rates of the Fe2O3-TiO2 films in 5 M HCl appear to be significantly smaller than those of the passive films on the Fe-Ti alloy films and the Fe-Ti alloys in the same solution.

本文言語英語
ページ(範囲)2818-2826
ページ数9
ジャーナルJournal of the Electrochemical Society
145
8
DOI
出版ステータス出版済み - 1998 8月

フィンガープリント

「Comparison of corrosion resistances between Fe2O3-TiO2 artificial passivation film and passivation film on Fe-Ti alloy」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル