Effect of Nitrogen on Sigma Transformation in Duplex Stainless Steel Weld Metal at High Temperatures

Y. S. Sato, H. Kokawa, T. Kuwana

研究成果: 会議への寄与学会論文査読

2 被引用数 (Scopus)

抄録

A type 329J4L duplex stainless steel was GTA(gas tungstenarc)-welded without filler material in argon-nitrogen mixed gas atmosphere. Weld metals with different nitrogen contents were annealed a 1900-1300K. Time-Temperature-Precipitation (TTP) diagrams for sigma initiation and change in sigma content at 1200K during annealing were measured with the base and weld metals. In weld metals, nose temperature was around 1200K and initiation time of sigma was about 102.5s, regardless of nitrogen content. Nitrogen didn't affect the nose temperature and initiation time of sigma. On the other hand, the increase in nitrogen content decreased sigma content over annealing time of 105s in the weld metals. The effect of sigma content on fracture toughness of weld metal was examined using Small Punch (SP) test which can evaluate fracture toughness of small area as SP energy. A small amount of sigma in the weld metal led to a marked decrease in the SP energy. Crystallographic characteristics of sigma initiation were examined using Orientation Imaging Microscopy (OIM).

本文言語英語
ページ131-136
ページ数6
出版ステータス出版済み - 1998
イベントTrends in Welding Research: Proceedings of the 5th International Conference - Pine Mountain, GA, 米国
継続期間: 1998 6月 11998 6月 5

会議

会議Trends in Welding Research: Proceedings of the 5th International Conference
国/地域米国
CityPine Mountain, GA
Period98/6/198/6/5

フィンガープリント

「Effect of Nitrogen on Sigma Transformation in Duplex Stainless Steel Weld Metal at High Temperatures」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル