Effect of Ultra-High-Pressure Annealing on Defect Reactions in Ion-Implanted GaN Studied by Positron Annihilation

Akira Uedono, Hideki Sakurai, Jun Uzuhashi, Tetsuo Narita, Kacper Sierakowski, Shoji Ishibashi, Shigefusa F. Chichibu, Michal Bockowski, Jun Suda, Tadakatsu Ohkubo, Nobuyuki Ikarashi, Kazuhiro Hono, Tetsu Kachi

研究成果: ジャーナルへの寄稿学術論文査読

13 被引用数 (Scopus)

抄録

Herein, the annealing behaviors of defects in ion-implanted GaN are studied by positron annihilation, cathodoluminescence, scanning transmission electron microscopy, and atom probe tomography. Si or Mg ions are implanted into GaN to obtain 300 nm deep box profiles of the impurities. The samples are annealed up to 1480 °C under a N2 pressure of 1 GPa. For as-implanted GaN, the major defect species is identified as Ga-vacancy-type defects. After annealing above 1000 °C, vacancy clusters are introduced, and they remain even after 1480 °C annealing. For Mg-implanted GaN with the Mg concentration ([Mg]) ≤ 1018 cm−3, no large change in the depth distribution of Mg is observed before and after annealing at 1400 °C. For the sample with [Mg] = 1019 cm−3, however, Mg diffuses into the bulk, which is attributed to the over-doping of Mg and their vacancy-assisted diffusion. The Mg diffusion is suppressed, and the donor–acceptor pair emission is enhanced by sequential N-implantation, which is attributed to the reaction between Mg and vacancies under a N-rich condition. For the samples annealed at 1480 °C, an accumulation of Mg around dislocation loops and Mg clustering are enhanced by the N-implantation.

本文言語英語
論文番号2200183
ジャーナルPhysica Status Solidi (B): Basic Research
259
10
DOI
出版ステータス出版済み - 2022 10月

フィンガープリント

「Effect of Ultra-High-Pressure Annealing on Defect Reactions in Ion-Implanted GaN Studied by Positron Annihilation」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル