Effects of Cobalt Addition in Nanocrystalline Fe83.3Si4B8P4Cu0.7 Soft Magnetic Alloy

Yan Zhang, Parmanand Sharma, Akihiro Makino

研究成果: ジャーナルへの寄稿学術論文査読

39 被引用数 (Scopus)

抄録

Amorphous ribbons (∼5 mm in width and ∼20 μm in thickness) of Fe83.3-xCoxSi4B8P4Cu0.7 (x = 0C40 at%) alloys were made by single roller melt-spinning technique in air. Crystallization of ribbons takes place in two steps, i.e., primary and secondary. Nanocrystalline bcc Fe-Co grains (size ∼15-30 nm) were precipitated from the amorphous matrix during primary crystallization (temperature range ∼350 °550 °C). Addition of Co leads to increase in primary crystallization temperature (Tx1), and the difference between the primary and the secondary crystallization temperature (Tx2) tends to broaden with the increase in Co content. Lowest coercivity (∼5 A/m), highest saturation magnetization (∼195 emu/g) and a very low core loss of ∼0.32 W/kg (at 50 Hz and 1.5 T) were obtained for the ribbons with Co content ∼4 at%. Although bcc Fe has high solubility of Co, the soft magnetic properties were found to degrade for the Co contents >10 at%. Soft magnetic properties of Fe79.3Co4Si4B8P4Cu0.7 alloy are similar to Fe rich Fe85Si2B8P4Cu1 nanocrystalline alloy.

本文言語英語
論文番号6787090
ジャーナルIEEE Transactions on Magnetics
50
4
DOI
出版ステータス出版済み - 2014 4月 1

フィンガープリント

「Effects of Cobalt Addition in Nanocrystalline Fe83.3Si4B8P4Cu0.7 Soft Magnetic Alloy」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル