FeNi and Fe16N2 magnets prepared using leaching

Takayuki Kojima, Satoshi Kameoka, Masaki Mizuguchi, Koki Takanashi, An Pang Tsai

研究成果: Article査読

6 被引用数 (Scopus)


L10-type FeNi alloys and ¡AA-Fe16N2 are candidates for permanent magnets without precious metals, but they are difficult to prepare because atomic diffusion is extremely slow below the orderdisorder transition temperature of L10-FeNi (320°C) and because ¡AA-Fe16N2 is a metastable phase. Here, we report trials for preparing them using leaching, which is a method to obtain porous metals with a high surface area. We used such chemically active porous alloys as precursors for preparing L10-FeNi using the driving force of atomic diffusion and for preparing ¡AA-Fe16N2 using high reactivity with ammonia. No proofs for obtaining the L10-FeNi phase were observed, likely due to an Al impurity of 10 mol% and/or too small of a grain size. An Fe16N2 with ¡AA phase was obtained. Although the saturation magnetization was smaller than that of Fe, a large coercivity (up to 121kAm11) was obtained.

ジャーナルMaterials Transactions
出版ステータスPublished - 2019

ASJC Scopus subject areas

  • 材料科学(全般)
  • 凝縮系物理学
  • 材料力学
  • 機械工学


「FeNi and Fe16N2 magnets prepared using leaching」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。