Fractographic observations on Sm-Ba-Cu-O bulk superconductors fractured by tensile tests

K. Katagiri, K. Kasaba, Y. Shoji, A. Chiba, M. Tomita, T. Miyamoto, M. Murakami

研究成果: ジャーナルへの寄稿学術論文査読

17 被引用数 (Scopus)

抄録

The fracture surface morphology of top-seeded melt-grown SmBa2Cu3Ox bulk superconductors after tensile tests in 〈100〉 direction at room temperature was observed using SEM. There were voids with and without Ag particles of diameters ranging from 80 to <10 μm on the fracture surface of high density sample, while the size was 300 μm at the largest on the low density sample. Ag particles of 10 to 20 μm had the matching mate on the other side of the fracture surface. In the high density samples, the propagation of the crack was easily traced through the flow markings with steps on the fracture surface, while it was difficult to trace in low density samples.

本文言語英語
ページ(範囲)803-806
ページ数4
ジャーナルPhysica C: Superconductivity and its Applications
357-360
DOI
出版ステータス出版済み - 2001 8月

フィンガープリント

「Fractographic observations on Sm-Ba-Cu-O bulk superconductors fractured by tensile tests」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル