Fundamental study of Sn removal from hot metal by NH3 gas blowing

Naotaka Sasaki, Yu Ichi Uchida, Yu Ji Miki, Hidetoshi Matsuno

研究成果: Article査読

1 被引用数 (Scopus)


Development of a practical method of Sn removal in the steelmaking process is necessary from the viewpoints of promoting use of scrap procured in the market and reducing energy consumption. It is well known that Sn promotes surface cracks of billets in hot rolling by coexisting with Cu. Although various methods of Sn removal have been investigated in laboratory experiments, enough Sn removal efficiency for commercially use has not been obtained. In the present study, Sn removal from high-S hot metal by NH3 gas blowing was investigated in laboratory experiments as a new method of Sn removal. The laboratory experiment on Sn removal from hot metal was carried out using up to a 10 kgscale vacuum induction melting furnace. Sn removal was accelerated while blowing NH3 gas, and the evolution of gas bubbles were observed at the hot metal surface. Within the ranges of these experiments, higher temperature and higher concentrations of S and N were advantageous for Sn removal. The mechanism of the acceleration of Sn removal by NH3 gas blowing could be estimated that oversaturated N or H in hot metal made small bubbles to increase the hot metal surface for SnS evaporation. In the estimation of Sn removal ratio in plant-scale operation, it could reach 40%. For further rapid Sn removal, it was necessary to maximize [N] of hot metal by optimizing the lance height or flow rate of NH3 gas.

ジャーナルTetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan
出版ステータスPublished - 2016

ASJC Scopus subject areas

  • 凝縮系物理学
  • 物理化学および理論化学
  • 金属および合金
  • 材料化学


「Fundamental study of Sn removal from hot metal by NH3 gas blowing」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。