Improved critical current densities in MgB2 tapes with ZrB 2 doping

Xianping Zhang, Zhaoshun Gao, Dongliang Wang, Zhengguang Yu, Yanwei Ma, S. Awaji, K. Watanabe

研究成果: ジャーナルへの寄稿学術論文査読

20 被引用数 (Scopus)

抄録

MgB2/Fe tapes with 2.5-15 at. % ZrB2 additions were prepared through the in situ powder-in-tube method. The phases, microstructures, critical current density, and flux pinning were characterized by means of x-ray diffraction, scanning electron microscope, and magnetic and transport property measurements. Compared to the pure tape, a significant improvement in the in-field JC was observed for all the ZrB2 doped samples, while the critical temperature decreased slightly. The highest JC value was achieved for the 10 at. % doped sample. At 4.2 K, the transport J C increased by more than an order of magnitude than the undoped one in magnetic fields above 9 T. Nanoscale segregates or defects caused by the ZrB2 additions which act as effective flux pinning centers are proposed to be the main reasons for the improved JC field performance.

本文言語英語
論文番号132510
ジャーナルApplied Physics Letters
89
13
DOI
出版ステータス出版済み - 2006

フィンガープリント

「Improved critical current densities in MgB2 tapes with ZrB 2 doping」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル