TY - JOUR
T1 - Indirect exchange spring between FePt and Fe with a Ru interlayer
AU - Jiang, Jianhua
AU - Tezuka, Nobuki
AU - Inomata, K.
PY - 2006/7/1
Y1 - 2006/7/1
N2 - Indirect exchange spring in magnetron-sputtered FePt/Ru/Fe trilayers as well as multilayers have been investigated. Interlayer exchange coupling between FePt and Fe layers through a Ru spacer was obtained with an oscillation period of about 1 nm. Magnetic properties of FePt thin films with different nominal thicknesses deposited on MgO (1 1 0) substrates at 400 °C showed that 12.5 nm thick FePt film had both high coercivity and good squareness. In FePt/Ru/Fe trilayers, ferromagnetic coupling between the two magnetic layers was achieved with a 0.5 nm thick Ru layer, and the saturated magnetization was largely improved after using interlayer exchange coupling with Fe while the coercivity changed little, which indicated that indirect exchange spring was a promising approach for high-performance magnets. Multilayers with such structures had also been studied with different thickness ratio of the two magnetic layers and strong exchange coupling was achieved as Fe thickness ratio increased.
AB - Indirect exchange spring in magnetron-sputtered FePt/Ru/Fe trilayers as well as multilayers have been investigated. Interlayer exchange coupling between FePt and Fe layers through a Ru spacer was obtained with an oscillation period of about 1 nm. Magnetic properties of FePt thin films with different nominal thicknesses deposited on MgO (1 1 0) substrates at 400 °C showed that 12.5 nm thick FePt film had both high coercivity and good squareness. In FePt/Ru/Fe trilayers, ferromagnetic coupling between the two magnetic layers was achieved with a 0.5 nm thick Ru layer, and the saturated magnetization was largely improved after using interlayer exchange coupling with Fe while the coercivity changed little, which indicated that indirect exchange spring was a promising approach for high-performance magnets. Multilayers with such structures had also been studied with different thickness ratio of the two magnetic layers and strong exchange coupling was achieved as Fe thickness ratio increased.
KW - Exchange spring
KW - FePt
KW - Interlayer exchange coupling
KW - Magnetization
KW - Permanent magnet
UR - http://www.scopus.com/inward/record.url?scp=33645159721&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=33645159721&partnerID=8YFLogxK
U2 - 10.1016/j.jmmm.2005.08.009
DO - 10.1016/j.jmmm.2005.08.009
M3 - Article
AN - SCOPUS:33645159721
SN - 0304-8853
VL - 302
SP - 40
EP - 46
JO - Journal of Magnetism and Magnetic Materials
JF - Journal of Magnetism and Magnetic Materials
IS - 1
ER -