Magnetic properties and microstructure of the granular films processed by annealing FePt-based multilayers

T. O. Seki; Y. K. Takahashi; K. Hono

doi:10.1109/TMAG.2005.854693

Magnetic properties and microstructure of the granular films processed by annealing FePt-based multilayers

研究成果: Article › 査読

抄録

To explore the possibility of FePt-based soft/hard nanocomposite magnets, granular films were prepared by annealing Pt/Fe, FePt/Fe, and FePt/Fe ₃Pt multilayers. Although a high coercivity of 12 kOe was obtained by annealing the Fe₃Pt/FePt multilayers, only a small remanence was obtained due to random orientation of L1₀ FePt grains. By introducing oxygen during the film deposition, a few nanometer oxide particles were observed within the FePt grains and H_c increased at the expense of M_r. A possible way to achieve a higher value of (BH)_max is discussed based on the relationship between the microstructure and magnetic properties.

本文言語	English
ページ（範囲）	3799-3801
ページ数	3
ジャーナル	IEEE Transactions on Magnetics
巻	41
号	10
DOI	https://doi.org/10.1109/TMAG.2005.854693
出版ステータス	Published - 2005 10月
外部発表	はい

ASJC Scopus subject areas

電子材料、光学材料、および磁性材料
電子工学および電気工学

文献へのアクセス

10.1109/TMAG.2005.854693

他のファイルとリンク

引用スタイル

@article{1343e4ec0629434fb1e06fd42c114ea3,

title = "Magnetic properties and microstructure of the granular films processed by annealing FePt-based multilayers",

abstract = "To explore the possibility of FePt-based soft/hard nanocomposite magnets, granular films were prepared by annealing Pt/Fe, FePt/Fe, and FePt/Fe 3Pt multilayers. Although a high coercivity of 12 kOe was obtained by annealing the Fe3Pt/FePt multilayers, only a small remanence was obtained due to random orientation of L10 FePt grains. By introducing oxygen during the film deposition, a few nanometer oxide particles were observed within the FePt grains and Hc increased at the expense of Mr. A possible way to achieve a higher value of (BH)max is discussed based on the relationship between the microstructure and magnetic properties.",

keywords = "Coercivity, Energy product, Exchange coupling, Multilayer, Nanocomposite magnets",

author = "Seki, {T. O.} and Takahashi, {Y. K.} and K. Hono",

year = "2005",

month = oct,

doi = "10.1109/TMAG.2005.854693",

language = "English",

volume = "41",

pages = "3799--3801",

journal = "IEEE Transactions on Magnetics",

issn = "0018-9464",

publisher = "Institute of Electrical and Electronics Engineers Inc.",

number = "10",

}

TY - JOUR

T1 - Magnetic properties and microstructure of the granular films processed by annealing FePt-based multilayers

AU - Seki, T. O.

AU - Takahashi, Y. K.

AU - Hono, K.

PY - 2005/10

Y1 - 2005/10

N2 - To explore the possibility of FePt-based soft/hard nanocomposite magnets, granular films were prepared by annealing Pt/Fe, FePt/Fe, and FePt/Fe 3Pt multilayers. Although a high coercivity of 12 kOe was obtained by annealing the Fe3Pt/FePt multilayers, only a small remanence was obtained due to random orientation of L10 FePt grains. By introducing oxygen during the film deposition, a few nanometer oxide particles were observed within the FePt grains and Hc increased at the expense of Mr. A possible way to achieve a higher value of (BH)max is discussed based on the relationship between the microstructure and magnetic properties.

AB - To explore the possibility of FePt-based soft/hard nanocomposite magnets, granular films were prepared by annealing Pt/Fe, FePt/Fe, and FePt/Fe 3Pt multilayers. Although a high coercivity of 12 kOe was obtained by annealing the Fe3Pt/FePt multilayers, only a small remanence was obtained due to random orientation of L10 FePt grains. By introducing oxygen during the film deposition, a few nanometer oxide particles were observed within the FePt grains and Hc increased at the expense of Mr. A possible way to achieve a higher value of (BH)max is discussed based on the relationship between the microstructure and magnetic properties.

KW - Coercivity

KW - Energy product

KW - Exchange coupling

KW - Multilayer

KW - Nanocomposite magnets

UR - http://www.scopus.com/inward/record.url?scp=27744449947&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=27744449947&partnerID=8YFLogxK

U2 - 10.1109/TMAG.2005.854693

DO - 10.1109/TMAG.2005.854693

M3 - Article

AN - SCOPUS:27744449947

SN - 0018-9464

VL - 41

SP - 3799

EP - 3801

JO - IEEE Transactions on Magnetics

JF - IEEE Transactions on Magnetics

IS - 10

ER -

Magnetic properties and microstructure of the granular films processed by annealing FePt-based multilayers

抄録

ASJC Scopus subject areas

文献へのアクセス

他のファイルとリンク

フィンガープリント

引用スタイル