NITROGEN ABSORPTION OF STAINLESS STEEL WELD METAL BY GAS TUNGSTEN ARC WELDING.

Takeshi Kuwana, Hiroyuki Kokawa, Ken ichiro Naitoh

研究成果: Article査読

1 被引用数 (Scopus)

抄録

Using an arc atmosphere controlling chamber, effects of the welding conditions and atmosphere on the nitrogen content of the stainless steel weld metal by gas tungsten arc welding were investigated in comparison with those on the iron weld metal. The results are as follows: (1) The temperatures of stainless steel and iron molten pools were measured as about 1530 degree C and 1630 degree C, respectively. (2) The nitrogen content of stainless steel weld metal decreased with increasing the welding current, as well as that of iron weld metal. (3) The nitrogen content of stainless steel weld metal hardly dependend on the arc length, as well as that of iron weld metal. (4) The nitrogen content of stainless steel weld metal increased with increasing the travel speed, while that of iron weld metal hardly depended on the travel speed. (5) The nitrogen content of stainless steel weld metal increased with the nitrogen partial pressure at low nitrogen partial pressure region, and was constant at the nitrogen partial pressure region above 0. 2 atm in N//2-Ar gas mixture atmosphere, as well as that of iron weld metal. (6) The nitrogen absorption by stainless steel weld metal was discussed with equilibrium data.

本文言語English
ページ(範囲)99-105
ページ数7
ジャーナルYosetsu Gakkai Ronbunshu/Quarterly Journal of the Japan Welding Society
2
4
出版ステータスPublished - 1984 11月 1

ASJC Scopus subject areas

  • 材料力学
  • 機械工学
  • 表面、皮膜および薄膜
  • 金属および合金

フィンガープリント

「NITROGEN ABSORPTION OF STAINLESS STEEL WELD METAL BY GAS TUNGSTEN ARC WELDING.」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル