Oxide ion and electron transport properties in lanthanum silicate oxyapatite ceramics

Atsushi Mineshige, Hiroyuki Mieda, Mitsuaki Manabe, Takahiro Funahashi, Yusuke Daiko, Tetsuo Yazawa, Mina Nishi, Katsuhiko Yamaji, Teruhisa Horita, Koji Amezawa, Keiji Yashiro, Tatsuya Kawada, Hideki Yoshioka

研究成果: ジャーナルへの寄稿学術論文査読

13 被引用数 (Scopus)

抄録

An oxygen-excess-type lanthanum silicate (LSO) solid electrolyte with high chemical stability as well as high ion conductivity was developed by optimizing the chemical composition, La9.333 + x(Si6 - yAl y)O26 + 1.5x - 0.5y. It was found that La 10(Si5.8Al0.2)O26.9 (x = 0.667, y = 0.2) exhibited the highest conductivity among them, and addition of a small amount of iron was effective for the improvement of its chemical stability. The LSO specimen of x = 0.667 and y = 0.2 with iron addition (0.5 mol%) was chemically stable and had a conductivity of 5.6 × 10- 2 S cm- 1 under air at 1073 K, while its electronic conductivity was less than 2.0 × 10- 4 S cm- 1 at the same temperature. The oxygen tracer diffusion coefficient, DO* of this material was determined as 2.0 × 10- 8 cm2 s- 1 at 1073 K.

本文言語英語
ページ(範囲)555-558
ページ数4
ジャーナルSolid State Ionics
262
DOI
出版ステータス出版済み - 2014 9月 1

フィンガープリント

「Oxide ion and electron transport properties in lanthanum silicate oxyapatite ceramics」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル