Processing and photoluminescence properties of surface crystallized ZnO glass-ceramics

Hirokazu Masai, Takahiro Ueno, Tatsuya Toda, Yoshihiro Takahashi, Takumi Fujiwara

研究成果: ジャーナルへの寄稿学術論文査読

14 被引用数 (Scopus)

抄録

ZnO surface crystallized glass-ceramics were fabricated using K 2O-CaO-ZnO-B2O3-SiO2-Al 2O3 glass system. Precipitation of Zn-containing oxide crystallites was affected by the chemical composition of borate glass, especially the amount of Al2O3. Substitution of SiO 2 for B2O3 brought selective crystallization of ZnO without precipitation of α-Zn3B2O6. ZnO-precipitated glass-ceramics showed surface crystallization with submicron-sized crystallites, which assured transparency of these glass-ceramics. The obtained glass-ceramic shows free exciton emission, which is similar to emission of ZnO single crystal.

本文言語英語
ページ(範囲)3080-3084
ページ数5
ジャーナルJournal of Non-Crystalline Solids
356
52-54
DOI
出版ステータス出版済み - 2010 12月

フィンガープリント

「Processing and photoluminescence properties of surface crystallized ZnO glass-ceramics」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル