Synthesis and the physical properties of the single crystals of a new quaternary compound ErRh2B2C using molten copper as a flux

Toetsu Shishido, Jinhua Ye, Takahiko Sasaki, Takehiko Matsumoto, Tsuguo Fukuda

研究成果: ジャーナルへの寄稿学術論文査読

1 被引用数 (Scopus)

抄録

The single crystals of a. new quaternary compound ErRh2B2C have been obtained as thin plates in an atmosphere of helium by the flux method using molten copper. The single crystals show golden-colored luster and the maximum size obtained is about 1.0 × 1.0 × 0.02 mm3. This compound belongs to a tetragonal system and seems to be a derivative of ThCr2Si2 type; lattice parameter: a=0.36848 (2) nm, c=1.05520 (3) nm, V=1.4327 × 10-28 m3 and Z=2. The electrical resistivity parallel to the a-b plane decreases monotonically with decreasing temperature, but no superconductivity is observed down to 1.5K. The residual resistivity ratio, ρ(273 K)/ρ(1.5 K), is 1.38. Similar type new compounds of RRh2B2C were obtained for R=La-Er (except Eu and Tm) and Y by arc-melting synthetic method.

本文言語英語
ページ(範囲)1117-1120
ページ数4
ジャーナルJournal of the Ceramic Society of Japan
104
12
DOI
出版ステータス出版済み - 1996

フィンガープリント

「Synthesis and the physical properties of the single crystals of a new quaternary compound ErRh2B2C using molten copper as a flux」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル